| Category | Product | K-Value | Applications |
|
| Co-polymeric Emulsion PVC | PA 5470/5
  | 69 | Paste-making PVC with 3% vinyl acetate content. Produces medium-viscosity plastisols with good storage stability and slightly pseudoplastic rheology. The fusing temperature is lower than that of homopolymers due to the vinyl acetate content. |
| Co-polymeric Emulsion PVC | E 70 LF
| 70 | |
| Co-polymeric Plastisol Extender Resin | SA 1062/7
| 61 | Co-polymeric extender resin developed especially for automotive underbody-protective coatings. When blended with paste-making PVC grades, good viscosity-reducing properties together with a reduction in fusing temperature can be achieved. |
| Co-polymeric Plastisol Extender Resin | C 12/62 V
| 62 | Copolymeric Extender Resin which decrease the viscosity and lowers the fusion temperature |
| Homopolymeric Emulsion PVC | E 69 VS
| 68 | high viscous, pseudoplastic Paste-PVC with very good adhesion to KTL |
| Homopolymeric Emulsion PVC | E 70 CQ
| 70 | Extremely high-viscosity with pronounced pseudoplastic rheology. Blend with other resins to increase viscosity and maintain pseudoplastic rheology. Excellent heat stability. |
| Homopolymeric Emulsion PVC | EP 7091
| 70 | Standard product with high, pseudoplastic paste viscosity |
| Homopolymeric Plastisol Extender Resin | C 65 V
| 65 | Standard product with very good viscosity-reducing properties. |
| Homopolymeric Plastisol Extender Resin | EXT
| 66 | Extender resin with very good viscosity-reducing properties. Mechanical properties of the finished product are usually excellent. |